CW613, brass, is a readily extrudable leaded alpha/beta brass with a small Tin addition, which gives little bit of strength and resistance to corrosion. The lead gives free cutting properties. CW613 is available as extruded rods and flats which are typically used in builders’ hardware.
CHEMICAL COMPOSITION
| Elements | Min (%) | Max (%) |
| Cu | 59.00 | 60.00 |
| Pb | 1.60 | 2.50 |
| Sn | 0.20 | 0.50 |
| Fe | – | 0.40 |
| Al | – | 0.10 |
| Ni | – | 0.30 |
| Total Others | – | 0.20 |
| Zn | Remainder |
MECHANICAL PROPERTIES ACCORDING TO EN12165 (AS PER TEMPER H070)
| Range (mm) | From | To | UTS Min | PS Min | Elongation Min (%) | Hardness Min (HV) | Hardness Max (HV) |
| Round (Dia) | 1.5 | 75 | – | – | – | 70 | 170 |
| Hex (A/F) | 3 | 70 | – | – | – | 70 | 170 |
| Square (A/F) | 3 | 60 | – | – | – | 70 | 170 |
| Rectangle (Thickness) | 3 | 50 | – | – | – | 70 | 170 |
| PHYSICAL PROPERTIES |
| Physical Properties | Metric | English |
| Density | 8.40 g/cc | 0.303 lb/in3 |
| CTE, linear | 26.0 ᶙm/m-˚C | 14.4 ᶙin/in-˚F |
| Specific Heat Capacity | 0.380 J/g-˚C | 0.0908 BTU/lb-˚F |
| Thermal Conductivity | 113 W/m-K | 784 BTU-in/hr-ft²-˚F |
| Melting Point | 880-900 ˚C | 1620 – 1650 ˚F |
| Solidus | 880 ˚C | 1620 ˚F |
| Liquidus | 900 ˚C | 1650˚F |
| FABRICATION PROPERTIES |
| Forming | Suitability |
| Machinability (CuZn39Pb3 = 100 %) | 80.00% |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Worked | Excellent |
TYPICAL USES
- Architecture
- Builders Hardware