C36300 is a lead free material suited for the use in drinking water applications. C36300 can be used where no high mechanical stresses occur. Uses: A ductile alloy suitable for blanking, riveting, bending, hot forging and pressing, hot heading, up-setting large nuts & bolts and brazing rods.
CHEMICAL COMPOSITION
| Elements | Min (%) | Max (%) |
| Cu | 61.0 | 63.0 |
| Pb | 0.25 | 0.7 |
| Fe | – | 0.15 |
| P | 0.04 | 0.15 |
| Total Imp | – | 0.5 |
| Zn | Remainder |
Mechanical Properties According To ASTM B921 (As Per Temper HO2)
| Range (Inch) | Form | To | UTS Min (Ksi) | PS Min (Ksi) | ELo Min (%) | Hardness Min (HRB) | Hardness Max (HRB) |
| Round (Dia) | 0.059 | 0.5 | 63 | 28 | 10 | – | – |
| 0.5 | 1 | 55 | 26 | 12 | – | – |
| 1 | 2 | 48 | 24 | 20 | – | – |
| 2 | 2.9527 | 45 | 20 | 25 | – | – |
| Hex (A/F) | 0.1181 | 0.5 | 63 | 28 | 10 | – | – |
| 0.5 | 1 | 55 | 26 | 12 | – | – |
| 1 | 2 | 48 | 24 | 20 | – | – |
| 2 | 2.7559 | 45 | 20 | 25 | – | – |
| Square (A/F) | 0.1181 | 0.5 | 63 | 28 | 10 | – | – |
| 0.5 | 1 | 55 | 26 | 12 | – | – |
| 1 | 2 | 48 | 24 | 20 | – | – |
| 2 | 2.3622 | 45 | 20 | 25 | – | – |
| Rectangle (Thickness) | 0.1181 | 0.5 | 63 | 28 | 10 | – | – |
| 0.5 | 1 | 55 | 26 | 12 | – | – |
| 1 | 1.9685 | 48 | 24 | 20 | – | – |
| Range (MM) | Form | To | UTS Min (Mpa) | PS Min (Mpa) | ELo Min (%) | Hardness Min (HRB) | Hardness Max (HRB) |
| Round (Dia) | 1.5 | 12 | 430 | 190 | 10 | – | – |
| 12 | 25 | 380 | 180 | 12 | – | – |
| 25 | 50 | 330 | 165 | 20 | – | – |
| 50 | 75 | 310 | 135 | 25 | – | – |
| Hex (A/F) | 3 | 12 | 430 | 190 | 10 | – | – |
| 12 | 25 | 380 | 180 | 12 | – | – |
| 25 | 50 | 330 | 165 | 20 | – | – |
| 50 | 70 | 310 | 135 | 25 | – | – |
| Square (A/F) | 3 | 12 | 430 | 190 | 10 | – | – |
| 12 | 25 | 380 | 180 | 12 | – | – |
| 25 | 50 | 330 | 165 | 20 | – | – |
| 50 | 70 | 310 | 135 | 25 | – | – |
| Rectangle (Thickness) | 3 | 12 | 430 | 190 | 10 | – | – |
| 12 | 25 | 380 | 180 | 12 | – | – |
| 25 | 50 | 330 | 165 | 20 | – | – |
PHYSICAL PROPERTIES
| Melting Point – Liquidus °F | 1650 |
| Melting Point – Solidus °F | 1630 |
| Density lb/cu in. at 68 °F | 0.304 |
| Specific Gravity | 8.42 |
| Electrical Conductivity %IACS at 68 °F | 26 |
| Thermal Conductivity Btu/ sq ft/ ft hr/ °F at 68 °F | 51.5 |
| Specific Heat Capacity Btu/ lb / °F at 68 F | 0.088 |
FABRICATION PROPERTIES
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Fair |
| Coated metal Arc Welding | Not Recommended |
| Spot Weld | Fair |
| Seam Weld | Not Recommended |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | Good |
| Machinability Rating | 80 |
TYPICAL USES